タイトル	Oxygen Solid Solution Strengthened Pure Titanium Powder Materials
著者	Sun, Bin Sun, Bin
	Li, Shufeng Li, Shufeng
	Imai, Hisashi Imai, Hisashi
	Umeda, Junko Umeda, Junko
	Kondoh, Katsuyoshi Kondoh, Katsuyoshi
キーワード等	powder metallurgy
	titanium
	spark plasma sintering
	solid solution
	reinforce
抄録	The applications of Ti and its alloys are limited to high-performance products because of expensive cost and poor plastic formability. In order to develop a cost-effective processing route for pure Ti and its alloys, pure Ti powder was used as raw material and consolidated by different power metallurgy routes in this study. Warm compaction and cold compaction were employed to consolidate Ti powder and spark plasma sintering (SPS) was used as reference method. The obtained compacts were subsequently hot extruded. The microstructure and mechanical properties of the hot-extruded pure Ti were evaluated. It was found that the samples prepared by warm compaction showed a higher tensile strength of 973.6 MPa, a better elongation of 26% and a higher hardness of 389.8 Hv comparing with the other two methods. Solid solution strengthening of oxygen was the main reinforcement mechanism for the sample prepared by warm compaction in this study. The strengthening effect of oxygen was calculated as 769.8 MPa/mass.%.
公開者	大阪大学接合科学研究所
公開者の別表記	Joining and Welding Research Institute, Osaka University
公開者 (ヨミ)	オオサカダイガクセツゴウカガクケンキュウジョ
掲載誌名	Transactions of JWRI
巻	41
号	1
開始ページ	59
終了ページ	64
刊行年月	2012-06
ISSN	03874508
NCID	AA00867058
URL	http://hdl.handle.net/11094/23164
言語	英語

著者版フラグ	publisher
NII資源タイプ	紀要論文
ローカル資源タイプ	紀要論文
dcmi資源タイプ	text
DCTERMS.bibliographicCitation	Transactions of JWRI.41(1) P.59-P.64
DC.title	Oxygen Solid Solution Strengthened Pure Titanium Powder Materials
DC.creator	Sun, Bin
	Li, Shufeng
	Imai, Hisashi
	Umeda, Junko
	Kondoh, Katsuyoshi
DC.publisher	大阪大学接合科学研究所
DC.language" scheme="DCTERMS.RFC1766	英語
DCTERMS.issued" scheme="DCTERMS.W3CDTF	2012-06
DC.identifier" scheme="DCTERMS.URI	http://hdl.handle.net/11094/23164
DC.subject	powder metallurgy
	titanium
	spark plasma sintering
	solid solution
	reinforce
DCTERMS.abstract	The applications of Ti and its alloys are limited to high-performance products because of expensive cost and poor plastic formability. In order to develop a cost-effective processing route for pure Ti and its alloys, pure Ti powder was used as raw material and consolidated by different power metallurgy routes in this study. Warm compaction and cold compaction were employed to consolidate Ti powder and spark plasma sintering (SPS) was used as reference method. The obtained compacts were subsequently hot extruded. The microstructure and mechanical properties of the hot-extruded pure Ti were evaluated. It was found that the samples prepared by warm compaction showed a higher tensile strength of 973.6 MPa, a better elongation of 26% and a higher hardness of 389.8 Hv comparing with the other two methods. Solid solution strengthening of oxygen was the main reinforcement mechanism for the sample prepared by warm compaction in this study. The strengthening effect of oxygen was calculated as 769.8 MPa/mass.%.
citation_title	Oxygen Solid Solution Strengthened Pure Titanium Powder Materials
citation_author	Sun, Bin
	Li, Shufeng
	Imai, Hisashi
	Umeda, Junko
	Kondoh, Katsuyoshi
citation_publisher	大阪大学接合科学研究所
citation_language	英語
citation_date	2012-06
citation_journal_title	Transactions of JWRI
citation_volume	41
citation_issue	1
citation_firstpage	59
citation_lastpage	64
citation_issn	03874508
citation_public_url	http://hdl.handle.net/11094/23164
citation_keywords	powder metallurgy
	titanium
	spark plasma sintering
	solid solution
	reinforce

閲覧可能ファイル

論文情報

論文詳細を表示