タイトル	Diffusion Bonding of Titanium Aluminide and Low-Carbon Steel Using a Spark Plasma Sintering System
著者	Kohama, Kazuyuki Kohama, Kazuyuki
著者	Ito Kazuhiro Ito Kazuhiro
抄録	Diffusion bonding of titanium-aluminide based alloys(TiAl)and SS400 low-carbon steels was conducted at 600-800℃for 0-60 min using a spark plasma sintering(SPS)system,then bonding strength of the TiAl/SS400 joints were evaluated by shear tests. Compared to previous studies regarding diffusion bonding of TiAl and high-carbon steels,the TiAl/SS400 joints exhibited considerably higher bonding strength. The reason for this is presumably based on increase in bonding area and formation of thinner TiC-based layers at the bonding interface derived from the higher deformability and lower carbon content in SS400. In addition, Vickers hardness measured on the surface of the TiAl and SS400 samples significantly increased after bonding regardless of the bonding temperature, showing that TiAl/SS400 joints with high surface hardness can be fabricated using the SPS system.
公開者	大阪大学接合科学研究所
公開者の別表記	Joining and Welding Research Institute, Osaka University
公開者 (ヨミ)	オオサカダイガクセツゴウカガクケンキュウジョ
掲載誌名	Transactions of JWRI
巻	44
号	2
開始ページ	23
終了ページ	26
刊行年月	2015-12
ISSN	03874508
NCID	AA00867058
URL	http://hdl.handle.net/11094/57273
言語	英語
カテゴリ	紀要論文 Departmental Bulletin Paper
カテゴリ	Transactions of JWRI / Vol.44 No.2 (2015-12)

著者版フラグ	publisher
NII資源タイプ	紀要論文
ローカル資源タイプ	紀要論文
dcmi資源タイプ	text
DCTERMS.bibliographicCitation	Transactions of JWRI.44(2) P.23-P.26
DC.title	Diffusion Bonding of Titanium Aluminide and Low-Carbon Steel Using a Spark Plasma Sintering System
DC.creator	Kohama, Kazuyuki
DC.creator	Ito Kazuhiro
DC.publisher	大阪大学接合科学研究所
DC.language" scheme="DCTERMS.RFC1766	英語
DCTERMS.issued" scheme="DCTERMS.W3CDTF	2015-12
DC.identifier" scheme="DCTERMS.URI	http://hdl.handle.net/11094/57273
DCTERMS.abstract	Diffusion bonding of titanium-aluminide based alloys(TiAl)and SS400 low-carbon steels was conducted at 600-800℃for 0-60 min using a spark plasma sintering(SPS)system,then bonding strength of the TiAl/SS400 joints were evaluated by shear tests. Compared to previous studies regarding diffusion bonding of TiAl and high-carbon steels,the TiAl/SS400 joints exhibited considerably higher bonding strength. The reason for this is presumably based on increase in bonding area and formation of thinner TiC-based layers at the bonding interface derived from the higher deformability and lower carbon content in SS400. In addition, Vickers hardness measured on the surface of the TiAl and SS400 samples significantly increased after bonding regardless of the bonding temperature, showing that TiAl/SS400 joints with high surface hardness can be fabricated using the SPS system.
citation_title	Diffusion Bonding of Titanium Aluminide and Low-Carbon Steel Using a Spark Plasma Sintering System
citation_author	Kohama, Kazuyuki
citation_author	Ito Kazuhiro
citation_publisher	大阪大学接合科学研究所
citation_language	英語
citation_date	2015-12
citation_journal_title	Transactions of JWRI
citation_volume	44
citation_issue	2
citation_firstpage	23
citation_lastpage	26
citation_issn	03874508
citation_public_url	http://hdl.handle.net/11094/57273

閲覧可能ファイル

論文情報

論文詳細を表示