Characteristics of Hot Extruded P/M Aluminum Alloy when Using the Rapidly Solidified Powder SWAP Process

Imai, Hisashi; Kawakami, Masashi; Kondoh, Katsuyoshi; Otsuka, Isamu; Izaki, Hiroshi

このアイテムのアクセス数:81件（2022-06-25 07:47 集計）

このアイテムへのリンクには次のURLをご利用ください:http://hdl.handle.net/11094/7025

閲覧可能ファイル

ファイル	フォーマット	サイズ	閲覧回数	説明
jwri36_02_033	pdf	718 KB	375

論文情報

タイトル	Characteristics of Hot Extruded P/M Aluminum Alloy when Using the Rapidly Solidified Powder SWAP Process
著者	Imai, Hisashi Imai, Hisashi
	Kawakami, Masashi Kawakami, Masashi
	Kondoh, Katsuyoshi Kondoh, Katsuyoshi
	Otsuka, Isamu Otsuka, Isamu
	Izaki, Hiroshi Izaki, Hiroshi
キーワード等	Aluminum alloy
	Spinning Water Atomization Process (SWAP)
	Hot extrusion
抄録	The characteristics of hot extruded aluminum alloy when using the rapidly solidified powder Spinning Water Atomization Process (SWAP) have been investigated. SWAP is one of advanced powder processing technologies to prepare high-performance powder particles with fine microstructures. In this study, A7075 aluminum alloy powder were produced by SWAP, and no intermetallic compound was detected in the raw powder. Microstructures and micro-hardness dependence on annealing temperature has been examined. Mechanical properties of the powder metallurgy (P/M) aluminum alloys consolidated by hot extrusion were superior to those of wrought alloys using ingot billets. A7075 wrought P/M alloys via T5 heat treatment show yield stress of 370 MPa and elongation of 15 % at the extrusion temperature of 623 K.
公開者	大阪大学接合科学研究所
公開者の別表記	Joining and Welding Research Institute, Osaka University
公開者 (ヨミ)	オオサカダイガクセツゴウカガクケンキュウジョ
掲載誌名	Transactions of JWRI
巻	36
号	2
開始ページ	33
終了ページ	38
刊行年月	2007-12
ISSN	03874508
NCID	AA00867058
URL	http://hdl.handle.net/11094/7025
言語	英語
カテゴリ	紀要論文 Departmental Bulletin Paper
カテゴリ	Transactions of JWRI / Vol.36 No.2 (2007-12)

著者版フラグ	publisher
NII資源タイプ	紀要論文
ローカル資源タイプ	紀要論文
dcmi資源タイプ	text
DCTERMS.bibliographicCitation	Transactions of JWRI.36(2) P.33-P.38
DC.title	Characteristics of Hot Extruded P/M Aluminum Alloy when Using the Rapidly Solidified Powder SWAP Process
DC.creator	Imai, Hisashi
	Kawakami, Masashi
	Kondoh, Katsuyoshi
	Otsuka, Isamu
	Izaki, Hiroshi
DC.publisher	大阪大学接合科学研究所
DC.language" scheme="DCTERMS.RFC1766	英語
DCTERMS.issued" scheme="DCTERMS.W3CDTF	2007-12
DC.identifier" scheme="DCTERMS.URI	http://hdl.handle.net/11094/7025
DC.subject	Aluminum alloy
	Spinning Water Atomization Process (SWAP)
	Hot extrusion
DCTERMS.abstract	The characteristics of hot extruded aluminum alloy when using the rapidly solidified powder Spinning Water Atomization Process (SWAP) have been investigated. SWAP is one of advanced powder processing technologies to prepare high-performance powder particles with fine microstructures. In this study, A7075 aluminum alloy powder were produced by SWAP, and no intermetallic compound was detected in the raw powder. Microstructures and micro-hardness dependence on annealing temperature has been examined. Mechanical properties of the powder metallurgy (P/M) aluminum alloys consolidated by hot extrusion were superior to those of wrought alloys using ingot billets. A7075 wrought P/M alloys via T5 heat treatment show yield stress of 370 MPa and elongation of 15 % at the extrusion temperature of 623 K.
citation_title	Characteristics of Hot Extruded P/M Aluminum Alloy when Using the Rapidly Solidified Powder SWAP Process
citation_author	Imai, Hisashi
	Kawakami, Masashi
	Kondoh, Katsuyoshi
	Otsuka, Isamu
	Izaki, Hiroshi
citation_publisher	大阪大学接合科学研究所
citation_language	英語
citation_date	2007-12
citation_journal_title	Transactions of JWRI
citation_volume	36
citation_issue	2
citation_firstpage	33
citation_lastpage	38
citation_issn	03874508
citation_public_url	http://hdl.handle.net/11094/7025
citation_keywords	Aluminum alloy
	Spinning Water Atomization Process (SWAP)
	Hot extrusion

閲覧可能ファイル

論文情報

論文詳細を表示